Carbon Steel Wire Rod SAE1012
The WIRE ROD WIRE ROD SAE1012
Carbon steel wire rod SAE1012 has good plasticity and reliability, with a tensile strength of 380-450MPa, a yield strength of 220-330MPa, and an elongation of 25-35%.
These mechanical properties make SAE1012 wire widely adaptable in many application fields.
The carbon content is less than 0.15%, the manganese content is about 0.30-0.60%, and the sulfur and phosphorus contents are relatively low.
SAE1012 wire rod production process
Raw material preparation: The production of low carbon wire rod SAE1012 requires the preparation of suitable raw materials. It is usually produced by hot rolling.
Smelting: During the smelting process, the content of various elements needs to be controlled.
Rolling: The smelted molten steel is poured into the mold for rolling to form the initial shape of the wire.
Drawing: Gradually reduce the diameter of the wire to achieve the required size and precision.
Surface treatment: Cleaning, lubrication, etc.
Application
Automotive manufacturing: Low carbon steel wire SAE1012 is often used to manufacture automotive parts, such as body parts, chassis and wheels.
Mechanical manufacturing: In mechanical manufacturing, hot rolled steel wire rod SAE1012 is used to manufacture various mechanical parts, such as bearings, gears, connecting rods, etc.
Building structure: Hot rolled alloy steel wire rod SAE1012 is also widely used in structural buildings, such as making beams, columns, frames and other parts.